|DOI / URL||link|
|Title (Primary)||Thermoanalytische Charakterisierung strahlengehärteter Polymerfilme - Thermal characterization of radiation-cured polymer films|
|Author||Hösselbarth, B.; Friese, K.; Geyer, W.;|
|Journal||Journal of Thermal Analysis and Calorimetry|
|Department||SEEFO; ANA; GM; SANA;|
Thermo-oxidative and thermo-mechanical stabilities of radiation-cured acrylates and epoxides were examined by TG, DMA and DSC.
The polymeric trifunctional acrylates PETIA, TMPTA and THEIC displayed the highest temperatures of onset of degradation. The high crosslinking density of the films resulted in an almost temperature-independent complex E-modulus, as measured by DMA. With increasing degree of ethoxylation or propoxylation of the monomers, decreases in thermal stability and strength were found. For difunctional polymeric acrylates and epoxides, the glass transition temperature was measured.
|Persistent UFZ Identifier||https://www.ufz.de/index.php?en=20939&ufzPublicationIdentifier=8713|
|Hösselbarth, B., Friese, K., Geyer, W. (1998):
Thermoanalytische Charakterisierung strahlengehärteter Polymerfilme - Thermal characterization of radiation-cured polymer films
J. Therm. Anal. Calorim. 52 (1), 145 - 155